美国陶氏DOW AMPLIFY TY 1351 优异的聚酰胺附着力

AMPLIFY™ TY 1351
Functional Polymer
陶氏塑料
产品说明
AMPLIFY™ TY 1351 Functional Polymer is a maleic anhydride grafted (MAH) polymer. In tie layers for flexible packaging, AMPLIFY TY 1351 Functional Polymer promotes
adhesion of Polyethylene to barrier polymers such as polyamide and other polar substrates.
Main Characteristics:
Excellent adhesion to polyamide
Excellent physical properties
Wide range of process and service temperature
For blown and cast film
Complies with:
US FDA 21 CFR 175.105
EU, No 10/2011
Consult the regulations for complete details.
基本信息
机构评级FDA 21 CFR 175.105 欧洲 No 10/2011
形式粒子
物理性能额定值单位制测试方法
密度 0.923 g/cm³ ASTM D792
熔流率(熔体流动速率) (190°C/2.16 kg) 2.1 g/10 min ASTM D1238, ISO 1133
MAH 接枝水平 1 Low 内部方法
薄膜额定值单位制测试方法
膜耐刺穿性 (51 μm) 11.6 J/cm³ 内部方法
割线模量 ASTM D882
2% 正割, MD : 51 μm 209 MPa ASTM D882
2% 正割, TD : 51 μm 229 MPa ASTM D882
抗张强度 ASTM D882
MD : 屈服, 51 μm 10.5 MPa ASTM D882
TD : 屈服, 51 μm 11.3 MPa ASTM D882
MD : 断裂, 51 μm 36.1 MPa ASTM D882
TD : 断裂, 51 μm 29.2 MPa ASTM D882
伸长率 ASTM D882
MD : 断裂, 51 μm 690 % ASTM D882
TD : 断裂, 51 μm 690 % ASTM D882
落锤冲击 (51 μm) 260 g ASTM D1709
埃尔曼多夫抗撕强度 2 ASTM D1922
MD : 51 μm 750 g ASTM D1922
TD : 51 μm 1100 g ASTM D1922
热性能额定值单位制测试方法
维卡软化温度 98.9 °C ASTM D1525
溶融温度(DSC) 123 °C 内部方法
光学性能额定值测试方法
光泽度 (45°, 50.8 μm) 70 ASTM D2457
挤压说明
Recommended Melt Temperature - 400-446°FFabrication Conditions for Blown Film
Screw Size: 2.5 in. (63.5 mm); 24:1 L/D
Screw Type: Barrier screw
Die Gap: 70 mil (1.8 mm)
Melt Temperature: 430°F (221°C)
Output: 6 lb/hr/in of die circumference
Die diameter: 6 in
Blow-Up Ratio: 2.5:1
Screw Speed: 70 rpm
备注
1. Low: 0.5 wt%
2. Method B