AMPLIFY™ TY 1352
Functional Polymer
陶氏塑料
产品说明
AMPLIFY™ TY 1352 Functional Polymer is a maleic anhydride grafted (MAH) polymer. In tie layers for flexible packaging, AMPLIFY TY 1352 Functional Polymer promotes
adhesion of Polyethylene to barrier polymers such as polyamide and ethylene vinyl alcohol (EVOH) and other polar substrates.
Main Characteristics:
Excellent adhesion to polyamide and EVOH
Excellent physical properties
Wide range of process and service temperature
For blown and cast film
Complies with:
US FDA 21 CFR 175.105
EU, No 10/2011
Consult the regulations for complete details.
基本信息
机构评级FDA 21 CFR 175.105 欧洲 No 10/2011
形式粒子
物理性能额定值单位制测试方法
密度 0.922 g/cm³ ASTM D792
熔流率(熔体流动速率) (190°C/2.16 kg) 1.0 g/10 min ASTM D1238
MAH 接枝水平 1 Low 内部方法
机械性能额定值单位制测试方法
抗张强度 ASTM D638
屈服 11.9 MPa ASTM D638
断裂 33.3 MPa ASTM D638
伸长率 (断裂) 2000 % ASTM D638
弯曲模量 - 2% 正割 351 MPa ASTM D790
薄膜额定值单位制测试方法
膜耐刺穿性 (51 μm) 19.9 J/cm³ 内部方法
割线模量 ASTM D882
2% 正割, MD : 51 μm 229 MPa ASTM D882
2% 正割, TD : 51 μm 280 MPa ASTM D882
抗张强度 ASTM D882
MD : 屈服, 51 μm 11.7 MPa ASTM D882
TD : 屈服, 51 μm 12.0 MPa ASTM D882
MD : 断裂, 51 μm 41.4 MPa ASTM D882
TD : 断裂, 51 μm 34.5 MPa ASTM D882
伸长率 ASTM D882
MD : 断裂, 51 μm 580 % ASTM D882
TD : 断裂, 51 μm 620 % ASTM D882
落锤冲击 (51 μm) 600 g ASTM D1709
埃尔曼多夫抗撕强度 2 ASTM D1922
MD : 51 μm 600 g ASTM D1922
TD : 51 μm 1100 g ASTM D1922
热性能额定值单位制测试方法
维卡软化温度 104 °C ASTM D1525
溶融温度(DSC) 125 °C 内部方法
光学性能额定值测试方法
光泽度 (45°) 65 ASTM D2457
挤出额定值单位制
熔体温度 210 到 230
http://xufuyou8753.b2b168.com
欢迎来到东莞市塑佳高分子原料有限公司网站, 具体地址是广东省东莞市樟木头镇先威路75号10栋103,老板是许斌耀。
主要经营塑料相关产品。
单位注册资金单位注册资金人民币 100 - 250 万元。
本公司产品好,产业规模属国内水平高,产品具有特色,规格比较齐全,质量保证体系规范。欢迎来订购,谢谢!