AMPLIFY™ TY 1354 Functional Polymer 陶氏塑料 产品说明 AMPLIFY™ TY 1354 Functional Polymer is a maleic anhydride grafted (MAH) polymer. In tie layers for flexible packaging, AMPLIFY TY 1354 Functional Polymer promotes adhesion of Polyethylene to barrier polymers such as polyamide and other polar substrates. Main Characteristics: Excellent adhesion to polyamide Excellent physical properties Wide range of process and service temperature For blown and cast film Complies with: US FDA 21 CFR 175.105 (c)(5) EU, No 10/2011 Consult the regulations for complete details. 基本信息 机构评级 FDA 21 CFR 175.105 欧洲 No 10/2011 形式 粒子 物理性能 额定值 单位制 测试方法 密度 0.920 g/cm³ ASTM D792 熔流率(熔体流动速率) (190°C/2.16 kg) 3.0 g/10 min ASTM D1238, ISO 1133 MAH 接枝水平 1 Low 内部方法 薄膜 额定值 单位制 测试方法 膜耐刺穿性 (51 µm) 9.51 J/cm³ 内部方法 割线模量 ASTM D882 2% 正割, MD : 51 µm 214 MPa ASTM D882 2% 正割, TD : 51 µm 240 MPa ASTM D882 抗张强度 ASTM D882 MD : 屈服, 51 µm 11.2 MPa ASTM D882 TD : 屈服, 51 µm 11.5 MPa ASTM D882 MD : 断裂, 51 µm 35.2 MPa ASTM D882 TD : 断裂, 51 µm 31.2 MPa ASTM D882 伸长率 ASTM D882 MD : 断裂, 51 µm 730 % ASTM D882 TD : 断裂, 51 µm 750 % ASTM D882 落锤冲击 (51 µm) 210 g ASTM D1709 埃尔曼多夫抗撕强度 2 ASTM D1922 MD : 51 µm 890 g ASTM D1922 TD : 51 µm 1100 g ASTM D1922 热性能 额定值 单位制 测试方法 维卡软化温度 98.9 °C ASTM D1525 溶融温度(DSC) 123 °C 内部方法 光学性能 额定值 测试方法 光泽度 (45°, 50.8 µm) 66 ASTM D2457 挤压说明 Recommended Melt Temperature - 400-446°FFabrication Conditions for Blown Film Screw Size: 2.5 in. (63.5 mm); 24:1 L/D Screw Type: Barrier screw Die Gap: 70 mil (1.8 mm) Melt Temperature: 430°F (221°C) Output: 6 lb/hr/in of die circumference Die diameter: 6 in Blow-Up Ratio: 2.5:1 Screw Speed: 70 rpm 备注 1. Low: 0.5 wt% 2. Method B